A Study on Static Strength of Fillet Welded Joint for Ship Structure-Effect of Inclined Angle, Partial Joint Penetration, Gap
Static Strength Fillet Welded Joint, Inclined Angle Partial Joint Penetration Gap
2009/4/30
The effect of inclined angle on static strength of fillet welded joint for inclined hold frame at forward and afterward hold is studied. In this study normal shear strength of the inclined fillet wel...
Effect of Grooving on Static Strength of Fillet Welded Joint for Ship Structure under Compressive Stress Condition applied by bending moment (2nd Report)
Fillet Welded Joint Corrosion Grooving Local Strength of Ship Structure Static Strength
2009/4/29
Corrosion of structural members of ships is one of the main problems for ship safety.
In this report effect of grooving on static strength of corroded fillet welded joints for ship structure is inves...
Influence of Weld Heat Input and Texture of Base Metal on Brittle Crack Propagation Behavior along Welded Joint-Numerical Simulation of Brittle Crack Propagation along Welded Joint （2nd Report）
Brittle Crack Propagation Behavior Brittle Crack Propagation Welded Joint
2009/4/14
In the previous paper, influence of applied stress, residual stress and toughness of welded joint on brittle crack propagation was analyzed based on a fracture mechanics model developed by the authors...
Prediction of Fatigue Crack Propagation of Welded Joint under Variable Amplitude Loading
Fatigue Crack Propagation Welded Joint Variable Amplitude Loading
2009/4/1
Fatigue cracks may initiate and propagate at welded joints of marine structures due to repeated wave loading. When fatigue cracks are detected in service condition, it is preferable to have an evaluat...
Effect of Grooving Corrosion in the vicinity of Fillet Welded Joint on Ultimate Strength of Hold Frame
grooving corrosion elasto-plastic
2009/3/27
Corrosion is said to be the most dominant factor which affects the physical life of ships. In this report, the effect of grooving corrosion in the vicinity of fillet welded joints on ultimate strength...
Influence of Residual Stress and Fracture Toughness on Brittle Crack Propagation Behavior along Welded Joint
plate thickness
2009/3/27
Recently, plate thickness in mega container ships has reached the very heavy thickness range, exceeding 70mm, not common in shipbuilding. The most important requirement for ensuring structural
FATIGUE DURABILITY EVALUATION OF TROUGH TO DECK PLATE WELDED JOINT OF ORTHOTROPIC STEEL DECK
orthotropic steel deck trough to deck plate welded detail fatigue durability evaluation
2008/12/17
The present study is intended as analysis investigations of fatigue durability of the trough to deck plate welded joint failed at weld root in deck plate. The investigations are carried out on the ba...