搜索结果: 1-9 共查到“石油化学工程 ZSM-5”相关记录9条 . 查询时间(0.156 秒)
以混合黏土原位合成多级孔道ZSM-5分子筛
混合黏土 原位晶化 多级孔道 ZSM-5分子筛
2018/4/3
以高岭土和硅藻土混合黏土作为研究对象，利用原位晶化技术和孔道控制技术，合成了具有多级孔道的ZSM5分子筛。采用粉末X射线衍射法（XRD）、N2静态吸附脱附法、电子扫描电镜（SEM）、红外光谱（FTIR）和热重差热（TGDTA）对所合成的样品进行分析表征。结果表明，原位晶化技术所合成的ZSM5分子筛结晶度为53%，晶粒大小约为2 μm，且含有中大孔结构和较大的比表面积及孔体积，具有高的...
选取硅铝比为45、150和250的H-ZSM-5分子筛，通过磷酸氢二铵水溶液饱和浸渍、干燥，以及在550℃的100%水蒸气气氛下水热处理2 h，制备出一系列不同磷负载量的磷改性ZSM-5分子筛样品。采用XRD、XRF、BET、NH3-TPD、27Al NMR、31P NMR等表征方法研究这些样品的磷氧化物分布状态及对骨架铝配位、物相、孔结构和酸性的影响。通过脉冲微反实验评价分析磷改性对ZSM-5分...
High Propylene Selectivity in Methanol-to-olefin Reaction over H-ZSM-5 Catalyst Treated with Phosphoric Acid
ZSM-5 Methanol-to-olefin Light olefin Phosphoric acid Propylene production MFI
2010/9/8
H-ZSM-5 zeolite was treated with phosphorus acid by impregnating H-ZSM-5 with aqueous solutions of phosphoric acid at various concentrations. H-ZSM-5 (P-HZSM-5) modified with phosphoric acid was used ...
Effects of Surface Modification of H-ZSM-5 Catalysts on Direct Transformation of Ethanol into Lower Olefins
Ethanol Propylene Direct synthesis Lanthanum modified H-ZSM-5
2009/8/4
Various H-ZSM-5 catalysts were assessed for ethanol conversion into lower olefins. Ethanol was converted to lower olefins over H-ZSM-5 catalyst without modification. The selectivities for ethylene an...
XAFS Characterization of Mo/ZSM-5 Catalysts for Methane Conversion to Benzene: Effect of Additives
Molybdenum carbide ZSM-5 Methane aromatization EXAFS
2009/7/27
ZSM-5 supported Mo catalysts for the dehydroaromatization reaction of methane were characterized by Mo K-edge EXAFS, NH3-TPD, and XPS techniques. Mo/ZSM-5 catalysts showed the maximum activity for be...
Catalyst Deactivation of High-silica ZSM-5 Zeolite Modified with Noble Metals during Vapor Phase Beckmann Rearrangement of Cyclohexanone Oxime
Beckmann rearrangement Catalyst deactivation High-silica zeolite
2009/7/24
High-silica ZSM-5 zeolites were synthesized by the addition of pentavalent ions, such as phosphorus and arsenic ions, to the mother gel for the zeolite preparation. The Beckmann rearrangement of cycl...
本发明提供了一种提高ZSM-5型系列分子筛催化剂活性的方法，包括用无机盐、无机酸或有机酸对所述催化剂进行一次以上的热交换处理和热焙烧过程。本发明还提供了利用经该活性提高后的ZSM-5型分子筛催化剂催化裂解碳四烷烃生产低碳烯烃的方法，可以在相对较低的温度下实现丁烷的裂解，提高三烯收率。
本项目的攻关:
进行两种新型分子筛催化材料ZSM-5/Y和ZSM-35分子筛的中试放大评价和工业放大合成研究.完成了两种分子筛工业原料放大合成实验,在工业生产装置上,获得纯度好,结晶度高的ZSM-5/Y和ZSM-35分子筛.研究并改进中试和工业放大产品在催化裂化催化剂中的应用特点.
本项目取得如下具体研究成果(其中ZSM-5/Y双组分分子筛部分的研究工作由我校和兰州石化研究院负责):
采用...